stick or small wire feed?

I am going to buy a welder soon.I had originally planned on oxy-act. setup,since I learned this in high school shop class,but dont want to store the tanks in my garage/basement.I looked at stick machines(225 buzz box) for about $200. around here.nice,but I have never used one and I will have to do some re-wiring for it.I have heard stick is hard to learn and Ive heard it is easy to learn.I tend to pick up mechanical skills quickly,so this may be the one.Fianally I looked at a wire feed,looks simple,but in my price range I will only get a unit with standard household current.I typically will only be working with 1/8" and 3/16" steel,sometimes1/4" I am worried the mig unit will not produce strong enough welds,yet the stick may be too strong for these thicknesses.Any suggestions would be helpful.
Old 11-08-2002, 02:00 AM
1grnlwn's Avatar
1grnlwn 1grnlwn is offline
LawnSite Bronze Member
Join Date: Aug 2001
Location: Central Illinois
Posts: 1,261
A wire welder would be perfect for you. 1/4 stuff can be welded with the small welders. You may have to make several passes. And 1/4" is thick for most small fab jobs. Don't get me wrong stick welding is tried and true American (sorry 75) work horse but it does take a fair amount of skill and a lot of practice. Especially with the thinner materials.

Old 11-08-2002, 02:16 AM
Bob Minney's Avatar
Bob Minney Bob Minney is offline
LawnSite Bronze Member
Join Date: Jan 2002
Location: The Hottest driest city next to Hades - Denver Colorado
Posts: 1,094
I use arc because thats what I know. Seemed easy to learn for me. I find thinner materials easier to work, but thats most of what I do. I can use Oxygen-Acetylene but I don't want the tanks at home either. Borrow from my brother when needed.
Never used wire feed so I can't compare.
If you want people to notice your faults, start giving advice.
Old 11-08-2002, 05:54 PM
Alan Alan is offline
Join Date: Mar 2000
Location: NW Vermont (Milton)
Posts: 1,185
I've got all three processes handy, torches(which I never weld with), stick, in the form of a 225 Lincoln "buzz box" and two MIGs, one Millermatic 130 and a Snap-On MM140. The Lincoln rarely gets used now. Only time I drag out the leads is if I have something heavy and relatively critical that needs low hydrogen electrodes to do the job correctly. Other than that it's usually the Snap-On that gets called upon. That's a 120 volt machine with 140 amp output at 100% duty cycle. It's on a wheeled carriage and abit too heavy to tote around so if I need to do something away from home I take the Miller and the generator. Both MIGS are normally using flux cored wire.

As for how hard to learn, I really can't say. MIG is easy to learn to do poor welds with. It's awful easy to put down beads that aren't stuck to anything. I learned stick first and I think that is the proper progression. If you can run stick then it's easy to make the switch to MIG.

With a bit of weave it's possible to run a properly prepared joint on 1/4" material with the flux cored. A bit harder with bare wire and gas at low currents but easy to do in two passes with the small machines. Bigger MIGs (more money) can run 1/4" beads with no problem.

Sorry for not having any real answers. All sorts of options though. I guess if I was starting from scratch I'd get a buzz box and a bunch of scrap steel. Glue it together and take the hammer to it. Bust things apart and observe how the weld failed, try again until you get welds that will take a beating and not snap.
Old 11-10-2002, 09:35 PM
Rob T Rob T is offline
LawnSite Member
Join Date: Oct 2002
Location: Central NJ
Posts: 165
If you can afford it buy a wire feed. Gas shielding is better than flux core and some machines will do both. Mig welding is the easiest to learn and is best for lighter guage material. For the lawn care operation mig is the way to go. The only drawback to mig is welding outside. If the wind is blowing, the gas shield will be blown away and the weld will be ruined by oxygen intrusion.
Over 29,000 lawns mowed since 1991, only 48,000 more and I can retire!
Old 12-08-2002, 02:23 PM
Clint Clint is offline
LawnSite Member
Join Date: Nov 2001
Location: Texas
Posts: 97
I would suggest a mig over stick, mig produces a much nicer weld, and you dont have to chip away slag. If you dont want to have tanks, they make a wire that does not require the gases, although, its about 5 times more expensive. it is actually better if you are welding outside as well, because the wind doesnt affect it, but this wire does splatter more and smoke quite a bit more.

<b>Morrison's Ground Maintenance</b>

Clint Morrison

Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is On

Forum Jump

Layout Style:

Powered by vBulletin® Version 3.8.6
Copyright ©2000 - 2016, Jelsoft Enterprises Ltd.
Copyright ©1998 - 2012, LawnSite.comô - Grand View Media
All times are GMT -4. The time now is 08:01 AM.

Page generated in 0.07859 seconds with 8 queries